| Melt flow rate (MFR) (230°C/2.16Kg) | 40g/10 min |
| Density (Method D) | 0.900g/cm³ |
| Flexural Modulus | 1150 MPa |
| Tensile Stress at Yield | 24 MPa |
| Tensile Elongation at Yield | 6% |
| IZOD Impact Strenght – Notched (23°C) | 5kJ/m2 |
| Heat Deflection Temperature B (0.45 MPa, Unannealed) | 90°C |
Product Characteristics
| Application | Housewares. Opaque Containers. Furniture |
| Processing Method | Injection Molding. TWIM |
| Market | Consumer Products. Rigid Packaging |
| Features | Good Dimensional Stability. HighFlow. Low Temperature Impact Resistance. |
CB 4000 MO is polypropylene impact copolymer. With its high flow, excellent dimensional stability, and superior balance of stiffness and impact, this grades is especially suitable for injection molding. Potential end use applications of CB 4000 MO include electrical appliance parts, automotive parts, food packaging and housewares.This grade is not intended for medical and pharmaceutical applications.
Packaging
Polypropylene (PP) pellet is typically packed in polyethylene bags with net weight of 25kg each. 50 bags are stacked on a flat wooden pallet (dimensions: 1100mm x 1300mm x 150mm) with net weight of 1250kg per pallet that is stretch-hood film wrapped. Upon agreement with a customer PP pellet can be packed into big bag sized for 1000kg on wooden pallet (dimensions: 1140mm x 1140mm x 150mm) without stretch-hood film wrapping. Polypropylene product of SOCAR Polymer cannot be transported in bulk using tank car.
Storage
Polypropylene product packed in 25kg bags or 1000kg big bags stacked on wooden pallet shall be stored in enclosed dry place preventing from direct sunlight at least 1 meter far from heaters, at temperature min. -15°C / max. 35°C, relative humidity max. 80%. Prior to processing PP product bags shall be kept in production area for at least 12 hours.